LEXAN™ 9034TG SHEET
PRODUCT DATASHEET
DESCRIPTION
LEXAN
TM
9034TG sheet is the standard general purpose LEXAN sheet. LEXAN
TM
9034TG sheet combines high impact and
temperature resistance with optical clarity and can be utilized for secondary glazing behind existing glazing for economical
protection against breakage or intrusion. LEXAN
TM
9034TG sheet can be cut, sawn, drilled and milled by using standard workshop
equipment and is therefore an excellent candidate for fabricating a wide range of indoor applications such as machine guards.
LEXAN
TM
9034TG sheet can be easily thermoformed into complex parts while retaining its excellent properties necessary for
demanding applications. LEXAN
TM
9034TG sheet may be decorated using a wide variety of modern techniques such as painting
and screen-printing.
TYPICAL PROPERTY VALUES

 These property values have been derived from resin data for the material used to produce this sheet product. Variation within normal
tolerances are possible for various colors. These typical values are not intended for specification purposes. If minimum certifiable properties
are required, please contact your local SABIC, Functional Forms representative. All values are measured at least after 48 hours storage at
23°C/50% relative humidity. All properties are measured on injection-molded samples. All samples are prepared according ISO 294.
™ Trademarks of SABIC
PROPERTY
TEST METHOD
UNITS
VALUE
PHYSICAL
Density
ISO 1183
g/cm³
1.2
Water Absorption, (23°C/sat)
ISO 62
%
0.35
Moisture Absorption (23°C / 50% RH)
ISO 62
%
0.15
MECHANICAL
Tensile Stress, yield, 50 mm/min
ISO 527
MPa
63
Tensile Strain, yield, 50 mm/min
ISO 527
%
6
Tensile Strain, break, 50 mm/min
ISO 527
%
120
Tensile Modulus, 1 mm/min
ISO 527
MPa
2350
Flexural Stress, yield, 2 mm/min
ISO 178
MPa
90
Flexural Modulus, 2 mm/min
ISO 178
MPa
2300
IMPACT
Izod Impact, unnotched 80*10*3 +23°C
ISO 180/1U
kJ/m²
NB
Izod Impact, notched 80*10*3 +23°C
ISO 180/1A
kJ/m²
70
Charpy Impact, notched, 23°C
ISO 179/2C
kJ/m²
35
THERMAL
Thermal Conductivity
ISO 8302
W/m-°C
0.2
CTE, 23°C to 80°C, flow
ISO 11359-2
1/°C
7.E-05
Ball Pressure Test, 125°C +/- 2°C
IEC 60695-10-2
-
PASSES
Vicat Softening Temp, Rate B/120
ISO 306
°C
145
Relative Temp Index, Elec
UL 746B
°C
130
Relative Temp Index, Mech w/impact
UL 746B
°C
130
Relative Temp Index, Mech w/oimpact
UL 746B
°C
130
Electrical
Volume Resistivity
IEC 60093
Ohm-cm
>1.E+15
Dielectric Strength, in oil, 3.2 mm
IEC 60243-1
kV/mm
17
UL RATING
Horizontal burn
UL94 HB
-
HB (0.75-1.65mm)