Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs)
KC-LINK™ with KONNEKT™ Technology for High-Eciency, High-Density Power Applications (Commercial Grade)
Table 2 – Performance & Reliability: Test Methods and Conditions (Commercial Only)
Stress Reference Test or Inspection Method
Terminal Strength KEMET Internal Appendix 1, Note: Force of 1.8 kg for 60 seconds
Board Flex AEC-Q200-005 Appendix 2, Note: 3.0 mm (minimum)
Solderability KEMET Custom Test
1. Board shear - SAC305 solder. Shear force of 1.8 kg (minimum)
2. Wetting balance - IEC 60068-2-69
Temperature Cycling
JESD22
Method JA-104
1,000 cycles (-55°C to +150°C), measurement at 24 hours ±4 hours after test conclusion
Biased Humidity
MIL-STD-202
Method 103
Load Humidity: 1,000 hours 85°C/85% RH and 200VDC. Add 100 K ohm resistor.
Measurement at 24 hours ±4 hours after test conclusion.
Low Volt Humidity: 1,000 hours 85C°/85%RH and 1.5 V. Add 100 K ohm resistor.
Measurement at 24 hours ±4 hours after test conclusion.
High Temperature Life
MIL-STD-202
Method 108/EIA-198
1,000 hours at 150°C with 1.0 X rated voltage applied
Storage Life
MIL-STD-202
Method 108
150°C, 0 VDC, for 1,000 hours.
Vibration
MIL-STD-202
Method 204
5 g for 20 minutes, 12 cycles each of 3 orientations. Note: Use 8" x 5" PCB 0.031" thick 7
secure points on one long side and 2 secure points at corners of opposite sides. Parts
mounted within 2" from any secure point. Test from 10 – 2,000 Hz.
Mechanical Shock
MIL-STD-202
Method 213
Method 213: Figure 1, Condition F Method 204: 5gs for 20 min, 12 cycles
Resistance to Solvents
MIL-STD-202
Method 215
Add aqueous wash chemical, OKEM Clean or equivalent
Environmental Compliance
Lead-free
Lead (Pb)-free, RoHS, and REACH compliant without exemptions.