Data Sheet

Discharge Temperature
（放电温度）
-10℃
0℃
23℃
60℃
Discharge Capacity(0.2 C5A)
（放电容量/0.2 C5A）
50%
80%
100%
95%
Shenzhen Cottcell Battery Technology Co.,Ltd
VER
：
A
Tel：[phone] Fax：[phone]
MODEL:IFR14500
E
Appearance（外观）
There shall be no sucu defect as flaw,crack,rust,leakage,which may adversely affect commercial value of battery.
电池外观应没有划痕、破裂、污迹、生锈、漏液等影响市场的缺陷存在。
Initial Performance Test（初始性能测试）
Table 2（表 2）
Temperature Dependence of discharge capacity（放电温度特性）
Cells shall be charged per 3.3.1 and discharged ＠0.2 C5A to 2.0 volts.Except to be discharged at temperaures
per Table 3. Cells shall be stored for 3 hours at the test temperature prior to discharging and then shall be discharged
at the test temperture.The capacity of a cell at each temperture shall be compared to the capacity achieved at 23℃
and the percentage shall be calculated.Each cell shall meet or exceed the requirements of Table 3.
电池按 3.3.1 规定充电。按表 3 的温度中放电，电池必须先在该试验温度中放置 3 个小时。在每一个温
度中的放电容量应不小于表 3 的要求。
Table 3（表 3）
Item
（项目）
Test Method Condition
（测试方法及条件）
Requirements
（要求）
（1）
Open-circuit Voltage
（开路电压）
The open-circuit voltage shall be measured within 24
hours after standard charge.
（标准充电后 24 小时内测量开路电压）
（2）
Intermal impedance
（初始内阻）
Intermal resistance measured at AC 1KHz after 50%
charge.
（半充电状态下，测量其 AC 1KHz 下的交流阻抗）
（3）
Minimal Rated Capacity
（最小额定容量）
The capacity on 0.2 C
5
A discharge till the voltage
tapered to 2.0V shall be measured after rested for
30min then finish standard charge.
（标准充电后，搁置 30 分钟，测量 0.2 C5A 放电
至 2.0V 截止电压所放出的容量）
Discharge Capacity（放电容量）